Spall TX2

HT Spall-TX2 is a rapid set, high strength low viscosity Polyurea repair material. This two part, 1:1 system is 100% solids and designed for rebuilding and repairing broken control joints and spalled concrete surfaces very quickly, as well as filling voids. HT Spall-TX2 is intended for use in damaged control joints, voids under concrete or tile, and warehouse spalls where there is no movement and damage is from steel wheels or small hard urethane wheels. HT Spall-TX2 has an extended pot life for larger jobs requiring more time.

Data Sheet:

Rebuilding control joints
Shallow spalls on bridge decks
Traffic area spalls & crack repairs
Grade matching
Floor repair
Stops additional damage
Fill & repair spall before coating
Used to “knit” cracked slabs
Fill voids under concrete or tile


Demonstration Videos:

   

100% Solids, No VOC's
Meets USDA and FDA Requirements
Cures from  -20° F to 130° F.
“Drive-Over” in 10 to 15 minutes
Produces High Strength Quickly
Self-leveling
Self Priming
Fast initial set; rapid gain to ultimate strengths.

Viscosity (Mixed)....................................................250 cps

Hardness, durometer (ASTM D2240)...............57 to 62D

Tensile Strength, PSI (ASTM D412)...........................4600

Tear Strength (ASTM D624).............................-lb/mil 489

Elongation % (ASTM D412).................................6% to 8%

Compressive Strength (neat)..............................3900 psi

(ASTM C109)            (with sand)............................4800 psi 

Bond Strength (ASTM 882-99)..............................3450 psi

22 oz. & 56 oz. Cartridges
1 Gallon Kit (with proportioning chambers)
2 Gallon
7 Gallon
10 Gallon Kits