HT Spall-TX is a rapid set, high strength low viscosity Polyurea repair material. This two part, 1:1 system is 100% solids and designed for rebuilding and repairing broken control joints, filling voids under tile and concrete, and spalled concrete surfaces very quickly. HT Spall-TX is intended for use in damaged control joints or warehouse spalls where there is no movement and damage is from steel wheels or small hard urethane wheels.

Data Sheet:

Rebuilding control joints
Shallow spalls on bridge decks
Traffic area spalls & crack repairs
Grade matching
Floor repair
Stops additional damage
Fill & repair spall before coating
Used to “knit” cracked slabs
Filling voids under concrete and tile


Demonstration Videos:

100% Solids, No VOC's
Meets USDA and FDA Requirements
Cures from  -20° F to 130° F.
“Drive-Over” in 10 to 15 minutes
Produces High Strength Quickly
Self-leveling
Self Priming
Fast initial set; rapid gain to ultimate strengths.

Viscosity (Mixed)..................................................250 cps
Hardness, durometer (ASTM D2240).............57 to 62D
Tensile Strength, PSI (ASTM D412).........................4600
Tear Strength (ASTM D624)...........................-lb/mil 489
Elongation % (ASTM D412)...............................6% to 8%
Compressive Strength (neat)............................ 3900 psi
(ASTM C109)    (with sand)..................................4800 psi
Bond Strength (ASTM 882-99)............................3450 psi

22 oz. & 56 oz. Cartridges
1 Gallon Kit (with proportioning chambers)
2 Gallon
7 Gallon
10 Gallon Kits