HT Capping Gel is a two component, 100% solids, high aspect ceramic-blend epoxy. It is a solvent free, high strength, high modulus, moisture insensitive, non-sag epoxy system. HT Capping Gel is ideal for capping ports and cracks in concrete, binding almost any material together, repairing holes, spalls, repairing rotted wood, install and repair anchor bolts, or hand rails, and as a high strength structural adhesive. HT Capping Gel can be used in concrete, hollow block, brick, stone and wood. It is ideal for use in a wide range of temperatures from 35°F to 110°F. It is an excellent choice where a high strength adhesive with maximum field reliability is desired.

Surface Preparation:

Surface must be clean and sound. It may be dry or damp, but free of standing water. Remove dust, grease, curing compounds, waxes, foreign particles and disintegrated materials.

Bulk Mixing:

Place 1 part by volume of component A and 1 part by volume of component B into a clean pail. Mix thoroughly until uniformly blended. Mix only the quantity that can be used within its pot life.

 

  • Crack injection sealer around ports and cracks.
  • Low odor.
  • Bonding agent (metal, concrete, brick, wood, stone, block).
  • Perfect for horizontal, overhead, and screen applications.  Non-sag/No-drip.
  • Excellent spall patching material.
  • Moisture insensitive.
  • For indoor and outdoor use. 
  • Will not soften over time.
  • Easy mix, 1 to 1 ratio.

Shelf Life..............................................2 years
Storage Conditions......................Below 95°F
Color (A+B)..............................Concrete Gray
Mix Ratio (by volume)................................1:1
Consistency (@ 78°F).......................Non-Sag
Temperature Range..................35°F – 110°F
Gel Time.........................................8 minutes
(100 gram mass @ 78°F)
Compressive Yield Strength...........9,800 psi
(7 days)
Linear Shrinkage.......................0.004 cm/cm